CHLORINATED POLYETHYLENE CPE

Chlorine，%

36±1

36±1

32±1

35±1

40±1

25±1

Heat of fuion ,J/g  ≤

2.0

2.0

20

20

5

2.0

Volatile ，%     ≤

0.30

0.30

0.30

0.30

0.30

0.30

Impurity particles ,  

unit/100g ≤

20

20

20

20

20

20

Shore Hardness A

， ≤

60

60

65

65

65

76

Tensile strength

，MPa≥

8.0

8.0

8.0

8.0

8.0

8.0

Elongation at break

，%  ≥

700

700

700

700

700

600

MFR 180℃×10kg

，g/10min

-

-

6-9

6-9

-

-

Main Applications

PVC impact modifier

Impact modifier

for high-speed extrusion of PVC products

FR-ABS

Flexible PVC

FR-ABS

Flexible PVC PE film

FR-ABS

Flexible PVC

Flame Resistance

PE film

PVC film

Impact modifier

for high-speed extrusion of  PVC products and

 stronger melt strength

Chlorine，%

25±1

30±1

30±1

36±1

36±1

36±1

36±1

36±1

36±1

40±1

Heat of fuion 

,J/g  ≤

40-60

1.5

1.5

1.5

1.5

1.5

1.5

1.5

1.5

1.5

Volatile 

,%     ≤

0.30

0.30

0.30

0.30

0.30

0.30

0.30

0.30

0.30

0.30

Impurity particles

 ,  unit/100g ≤

20

20

20

20

20

20

20

20

20

20

Shore Hardness 

,A ≤

76～86

65

65

55

55

55

60

60

60

60

Tensile strength

，MPa≥

-

8.0

8.0

8.0

8.0

8.0

8.0

8.0

8.0

8.0

Elongation at  break

，%  ≥

-

700

700

700

700

700

700

700

700

700

Mooney viscosity

ML(1+4)125℃

-

55~65

75~85

45~55

60~70

70~80

75~85

80~90

85~95

85~95

Main Applications

Mix with PE，used for thermoplastic wires

Wire&Cable

Hose

Low temperature products

Flexible magnet etc 

Low temperature products

Wire&Cable

Hose,etc

Wire&Cable

Hose,etc

Wire&Cable

Hose,etc

Wire&Cable

Hose,etc

Wire&Cable

Hose,etc

Wire&Cable

Hose,etc

Production of flame retardants,rubber

 cloth and oil resistant hoses